The dismantling of UNGG reactors in France will generate about 23 000 tons of radioactive graphite wastes. To manage these wastes, the radiological inventory and data on radionuclides (RN) location and speciation should be determined. 14C was identified as an important RN for disposal due to its high initial activity and the risk of release of a mobile organic fraction in environment, after water ingress into the disposal. Hence, the objective of this thesis, carried out in partnership with EDF, is to implement experimental studies to simulate and evaluate the impact of temperature, irradiation and graphite radiolytic corrosion on the in reactor behavior of 14C and its precursor, 14N. The obtained data are then used to study the thermal decontamination of graphite in presence of water vapor. The experimental approach aims at simulating the presence of 14C and 14N by the respective ion implantation of 13C and 14N or 15N in virgin graphite. This study shows that, in the temperature range reached during reactor operation, (100-500°C) and without radiolytic corrosion, 13C is thermally stable whatever the initial graphite structure. Moreover, irradiation experiments were performed on heated graphite (500°C) put in contact with a gas representative of the radiolysed coolant gas. They show the synergistic role played by the oxidative species and the graphite structure disorder on the enhancement of 13C mobility resulting in the gasification of the graphite surface and/or the selective oxidation of 13C more weakly bound than 12C. Concerning the pristine nitrogen, we showed first that the surface concentration reaches several hundred ppm (<500 ppm at) and decreases at deeper depths to about 160 ppm at.. Unlike implanted 13C, implanted nitrogen migrates at 500 ° C when the graphite is highly disordered (about 8 dpa) while remaining stable for a lower disorder rate (0.14 dpa). Experiments also show the synergistic role by electronic excitations and temperature that accelerate the transport of nitrogen to the surface of the graphite. Nitrogen seems to migrate in the form of molecular species (CN, C = N or C N). After eight hours of irradiation these species are, however, little or not released and blocked at the surface. The study of the thermal decontamination of graphite in presence of water vapor was performed with a thermogravimetric device coupled to a steam water generator device. The influence of temperature (700 ° C and 900 ° C) and of the relative humidity (50% RH and 90% RH) was tested with a wet gas fixed flow rate of 50 ml/min. Under these conditions, the selective oxidation of implanted carbon was confirmed.